​温州市铝蜂窝板防火A级检测 导热系数检测

铝蜂窝板ASTM E1530-19导热系数测试/ASTM E1530-11(2016)

蜂窝材料的有效导热系数是其非常重要的性能参考之一，目前铝蜂窝板导热系数测试标准主要为ASTM E1530标准，ASTME1530-19为版本标准，已取代ASTM E 1530-11(2016)，南京睿督与美国实验室提供涂料ASTME1530版本测试报告，

涂料导热系数测试标准-ASTM E1530/ ASTM E 1530-19
ASTM E1530 Standard Test Method for Evaluating the Resistance toThermal Transmission of Materials by the Guarded Heat Flow MeterTechnique。
ASTM E 1530用保护的热流计技术评定材料的耐传热性能的测试标准。

涂料导热系数测试方法-ASTM E1530/ ASTM E 1530-19
This test method covers a steady-state technique for thedetermination of the resistance to thermal transmission (thermalresistance) of materials in thickness of less than 25mm. This testmethod is useful for materials having a thermal resistance in therange from 10 to 400 ×10-4 m2 k/w thermal conductivity in theapproximate range, temperature range from 150 to 400K. It can beused outside these ranges with reduced accuracy for thickerspecimens and for thermal conductivity values up to 60W/(M.K)

ASTM E1530导热系数-样品要求
ASTM E1530样品要求：The recommended specimen configuration is a50.8±0.25mm diameter disk, having smooth flat and parallel faces.The thickness less than 25mm.

导热系数（thermalconductivity）:热流密度与温度梯度之比。即在单位温度梯度作用下物体内所产生的热流密度，单位为W/(m(℃)。导热系数是指在稳定传热条件下，1m厚的材料，两侧表面的温差为1度（K，℃），在一定时间内，通过1平方米面积传递的热量，单位为瓦/米.度（W/(m.K)，此处为K可用℃代替）。

导热系数与材料的组成结构、密度、含水率、温度等因素有关。非晶体结构、密度较低的材料，导热系数较小。材料的含水率、温度较低时，导热系数较小。

通常把导热系数较低的材料称为保温材料(我国标准规定，凡是平均温度不高于350℃时导热系数不大于0.12W/(m/K)的材料称为保温材料），而把导热系数在0.05瓦/米摄氏度以下的材料称为效保温材料。